Unfortunately, glass-glass PV modules are, similar to regular PV modules, subject to early life failures. A failure of growing concern are defects in the glass layer (s) of PV modules. The scale of decommissioned PV modules with glass defects will increase with the development of solar PV energy [ 7 ].

Glass breakage is a growing concern for the solar power plant operators. With the trend towards double glass sided modules as seen in Bifacials, or TOPCon with double glass sided construction, the changes in solar PV module design and materials mean breakages are now a bigger risk than ever.

A customer complaints research, on PV modules after two years of operation, observed glass breakage for 10% of the failure cases [ 28 ]. Another study on PV failures observed an even higher failure-share for glass breakage.

Studies have found that contact between glass and frames is linked to spontaneous breakage in some PV modules. A recommended solution is using rubbery silicone spacers which maintain separation between the glass and the frame. Many modules already use silicone gaskets, but some designs leave gaps where the glass directly touches the metal frame.

However, glass defects do not directly imply that PV modules endure internal damage nor that PV modules cannot continue to operate with minimal microcracks. Thus far, glass defects have been regarded as a failure beyond repair and no noticeable attempt has been made to develop reparation methods.

With the trend towards double glass sided modules as seen in Bifacials, or TOPCon with double glass sided construction, the changes in solar PV module design and materials mean breakages are now a bigger risk than ever. These breakages can be due to many reasons and no single factor bears the sole responsibility of operators' woes.